Instruction Manual

HK-D

HK-D-BA-e-1311 3

Table 2

No.

Material

HLD

Strength σ

b

(MPa)

1 Mild steel

350～522 374～780

2

High-carbon steel

500～710 737～1670

3

Cr steel

500～730 707～1829

4

Cr-V steel

500～750 704～1980

5

Cr-Ni steel

500～750 763～2007

6

Cr-Mo steel

500～738 721～1875

7

Cr-Ni-Mo steel

540～738 844～1933

8

Cr-Mn-Si steel

500～750 755～1993

9

Super strength steel

630～800 1180～2652

10

Stainless steel

500～710 703～1676

1.3 Types and specification

No.

Remarks

Standard Delivery

1

Main unit

1

2 D type impact device 1

3

Small supporting ring

1

Additional

Optional Delivery

1

Communication cable

with

DataView Software ATC 01

2 Printer

3+4 Nylon brush1 and 2

2. in case of choosing G type

impact device

5

Various non-conventional types of impact

devices

See table 3

6

Various non-conventional types of impact

supporting rings

See table 4

Table 3

Non conventional

impact devices

DC(D)/DL D+15 C G

Impacting energy

Mass of impact

body

11Mj

5.5g/7.2g

11mJ

7.8g

2.7mJ

3.0g

90mJ

20.0g

Test tip Hardness

Diameter of test tip

Material of test tip

1600HV

3mm

Tungsten

carbide

1600HV

3mm

Tungsten

carbide

1600HV

3mm

Tungsten

carbide

1600HV

5mm

Tungsten

carbide

I

mpact device

Diameter

Impact device

Length

Impact device

Weight

20mm

86(147)/

75mm

50g

20mm

162mm

80g

20mm

141mm

75g

30mm

254mm

250g

Max. hardness of

workpiece

940HV 940HV 1000HV 650HB

Mean roughness of

workpiece surface of

the Ra

1.6μm 1.6μm 0.4μm 6.3μm